Bayanin Tsari: 1050 Aluminum Circle/Disc (Aluminum Round Blank)

The 1050 Da'irar Aluminum (also known as Aluminum Disc) is a circular blank made from commercially pure aluminum (1000 jerin). With high aluminum content (≥99.5%), it offers excellent formability and surface treatment capabilities, making it an essential raw material for deep-drawn products like cookware, kayan aikin haske, kuma marufi.

1. Core Identification: Abun ciki, Mai fushi, da Ƙayyadaddun bayanai

  1. Haɗin Sinadari & Matsayi
    • Primary Standards: GB/T 3190, ASTM B209, ON 573.
    • Core abun da ke ciki: Aluminum (Al) content not less than 99.5%, with very low levels of impurities such as Silicon (Kuma) and Iron (Fe). No alloying elements are intentionally added.
    • Siffar Maɓalli: High purity with strict control over total impurities, ensuring excellent electrical conductivity, thermal watsin, da juriya na lalata.
  2. Common Supply Tempers
    • Sa fushi (Anane): Soft material with superior ductility, ideal for deep drawing and stamping​ processes (e.g., pot stretching).
    • H14 / H18 zafi (Taurin-Taurare): Cold-worked for increased strength and hardness, with reduced elongation. Suitable for shallow forming or parts requiring higher rigidity.
  3. Typical Specification Range
    • Kauri: 0.3 mm - 10.0 mm
    • Diamita: 100 mm - 1650 mm (Custom sizes available)
    • Ƙarshen Sama: Mai haske, niƙa (satin), mai rufi, da dai sauransu.

8011 aluminum da'ira

2. Key Properties and Characteristics

Kashi na Mallaka Takamaiman Ayyuka
Abubuwan Jiki​ Ƙananan yawa (~2.71 g/cm³), excellent electrical (~58% IACS) da thermal conductivity (~229 W/(MİI K)).
Juriya juriya​ Siffofin halitta, protective oxide film in air, offering good corrosion resistance.
Kayayyakin Injini​ Ƙarfin matsakaici, adjustable via cold working. ~95 MPa (Sa fushi), ~120 MPa (H14). Not heat-treatable.​
iya aiki​ Kyakkyawan zane mai zurfi, yin hatimi, lankwasawa, da weldability (TIG preferred).​ Anodizes uniformly with a fine finish.

3. Primary Production Process

Aluminum Ingot → Melting & Continuous Casting into Slab → Hot/Cold Rolling to Gauge → Continuous Annealing (to control temper) → Slitting/Cross Cutting → CNC Punching/Shearing into Circles → Deburring, Tsabtatawa, Surface Treatment → Inspection & Marufi.

4. Aikace-aikace na yau da kullun

  • Dafa abinci & Kayan aiki: Non-stick cookware body/base, tukwane, yin burodi, kettle base, murfi.
  • Haske & Lantarki: LED fitilu reflectors, inuwa, zafi nutse substrates, capacitor gidaje.
  • Marufi & Canisters: Food cans, ointment boxes, cosmetic cases, small chemical pails.
  • Ado & Hardware: Badges, farantin suna, bangarorin kayan aiki, general structural components.

5. Comparison with Common Similar Alloys

Alloy Al Content Core Differences & Halaye Typical Application Preference
1050​ ≥99.5% Best balance of purity and formability.​ Strict impurity control, excellent all-around workability, m. Various deep-drawn cookware, kayan dafa abinci, janar hardware.
1060​ ≥99.6% Dan kadan mafi girman tsarki fiye da 1050, offering better electrical/thermal conductivity at a slightly higher cost. Abubuwan lantarki, heat sinks where higher conductivity is critical.
3003​ ~ 98% Aluminum-Manganese alloy.​ Significantly higher strength and corrosion resistance than 1050. Can be strengthened by cold working. Sinadaran kwantena, ducts, architectural trim requiring higher strength.